碳当量

K = C + (Mn/6) + (Cr/5) + (Mo/4) + (Ni/15)

C (<= 0,5%) Mn(<= 1,0%) Cr (<= 1,0%) Mo (<= 0,6%) Ni (<= 3,5%)

K

33.667

CET = C + ((Mn+Mo)/10) + ((Cr + Cu)/20) + (Ni/40)

C (<= 0,5%) Mn(<= 1,0%) Cr (<= 1,0%) Cu Mo (<= 0,6%) Ni (<= 3,5%)

CET

26.500

CE = C + (Mn/6) + ((Cr + Mo + V)/5) + ((Ni + Cu)/15)

C (<= 0,5%) Mn(<= 1,0%) Cr (<= 1,0%) Mo (<= 0,6%) Ni (<= 3,5%) Cu (<= 0,5%) V (>= 0,2%)

CE

38.000

热输入

5 kJ/mm

电压U(伏) 电流I（安培）焊接速度(mm/s) 焊接速度(cm/min)

预热温度 Tp

25351.390 °C

千卡.效率厚度 t H-级别

冷却速率/速度 t8/5 (2-dimensional)

43.392 sec

冷却速率/速度 t8/5 (3-dimensional)

45452.487 sec

开裂因素 F2 预热温度 Tp 开裂因素 F3