Kohlenstoffäquivalent

Berechnung C-Äquivalente

K = C + (Mn/6) + (Cr/5) + (Mo/4) + (Ni/15)

C (<= 0,5%) Mn(<= 1,0%) Cr (<= 1,0%) Mo (<= 0,6%) Ni (<= 3,5%)

K

33.667

CET = C + ((Mn+Mo)/10) + ((Cr + Cu)/20) + (Ni/40)

C (<= 0,5%) Mn(<= 1,0%) Cr (<= 1,0%) Cu Mo (<= 0,6%) Ni (<= 3,5%)

CET

26.500

CE = C + (Mn/6) + ((Cr + Mo + V)/5) + ((Ni + Cu)/15)

C (<= 0,5%) Mn(<= 1,0%) Cr (<= 1,0%) Mo (<= 0,6%) Ni (<= 3,5%) Cu (<= 0,5%) V (>= 0,2%)

CE

38.000

Wärmeeinbringung Q

5 kJ/mm

Spannung U(Volt) Strom I(Ampere) Schweißgeschw. v(mm/s) Schweißgeschw. v(cm/min)

Vorwärmtemperatur Tp(°C)

25351.390 °C

therm. Wirkungsgrad k Dicke d(mm) H-Klasse(cm3/100g)

Abkühlgeschwindigkeit t8/5 (2-dimensional)

43.392 sec

Abkühlgeschwindigkeit t8/5 (3-dimensional)

45452.487 sec

Nahtfaktor F2 Vorwärmtemeperatur Tg gew. Nahtfaktor F3